High temperature alumina crucible
99% corundum ceramic crucible specifications: 5ml 10ml 15ml 20ml 25ml 30ml 50ml 100ml 150ml 200ml-2500ml.
Suitable for sample analysis and melt of laboratory metal, non-metallic materials.
Alumina crucibles’ features:
1, High purity: Al2O3> 99%, good chemical corrosion resistance
2, Good temperature endurance, long-term use at 1600 °C, 1800 °C short-term
3, Good rapid thermal shock resistance, not easy to burst
4 , Slip Casting with high density
Arc Straight alumina ceramic crucibles’ basic functions:
Name: straight alumina crucibles
Chemical Composition Al2O3 ≥ 99
R2O ≤ 0.2
Fe2O3 ≤ 0.1
SiO2 ≤ 0.2
Volume density (g/cm2) ≥ 3.80
Apparent porosity (%) <1
Bending strength (Mpa)> 350
Compressive strength (Mpa)> 12000
Dielectric constant Σ (1MHz) 2
The highest operation temperature (°C) 1800
Best roast container for making powder TV, rare earth materials, precious metals, and roasting high, medium and low ceramic capacitors, NTC, PTC piezoelectric ceramic and lithium cobalt oxide, lithium manganese oxide powder
Product detail pictures:
Related Product Guide:
We emphasize advancement and introduce new products into the market each year for Reliable Supplier U Type Textile Ceramic - High temperature alumina crucible – Heatfounder, The product will supply to all over the world, such as: Mozambique , Latvia , Kyrgyzstan , The working experience in the field has helped us forged a strong relations with customers and partners both in domestic and international market. For years, our products and solutions have been exported to more than 15 countries in the world and have been widely used by customers.
By Wendy from Argentina - 2015.10.09 19:07
The goods we received and the sample sales staff display to us have the same quality, it is really a creditable manufacturer.
By Muriel from Florida - 2015.11.06 10:04